PC 日本帝人 G-3430H 注塑级 低异向性 聚碳酸酯 原料

【供应】高流动PC/日本帝人/LV-2250吹塑级透明级pc代理原料技术数据性能项目试验条件[状态]测试方法测试数据数据单位基本性能吸水率24hr，in 23℃ASTM D-5700.20%物理性能比重JIS K-71121.20折射率ASTM D-5421585透光率3mm thickASTM D-100389%阻燃性0.38mmUL 94V-2机械性能压缩强度ASTM D-69576(770)Mpa(kgf/cm2)弯曲强度ASTM D-79090(915)Mpa(kgf/cm2)拉伸强度屈服点ASTM D-63861(620)Mpa(kgf/cm2)断裂点ASTM D-63881(830)Mpa(kgf/cm2)冲击强度值艾氏、带缺口厚度3.2mmASTM D-256880(90)J/m(kgf·cm/cm)拉伸率屈服点ASTM D-6386%断裂点ASTM D-638140%耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-256140(14)J/m(kgf·cm/cm)洛氏硬度ASTM D-78577M标度拉伸模量ASTM D-6382120(21600)Mpa(kgf/cm2)弯曲模量ASTM D-7902230(22700)Mpa(kgf/cm2)电气性能介电正切60HzASTM D-1500.0004耐导电径迹性（CTI）IEC 112300V绝缘破坏强度快速加压值厚度1.6mmASTM D-14930kv/mm耐电弧性ASTM D-495110sec体积电阻率ASTM D-2573×1016Ω.cm介电率60HzASTM D-1502.95介电正切106HzASTM D-1500.009介电率106HzASTM D-1502.9加工性能成型收缩率流动方向ASTM D-9550.5～0.7%垂直方向ASTM D-9550.5～0.7%热性能温度指数电学式厚度1.47mmUL 746B125°C冲击式厚度1.47mmUL 746B115°C非冲击式厚度1.47mmUL 746B125°C负荷挠曲温度负荷0.451MPa(4.6kgf/cm2)JIS K-7207143℃线膨胀系数流动方向ASTM D-696710-5cm/cm/℃垂直方向ASTM D-696710-5cm/cm/℃负荷挠曲温度负荷1.813MPa(18.6kgf/cm2)JIS K-7207133℃